Rating
| Concentration | 20 °C | 50 °C | Remark |
|---|---|---|---|
| concentration not stated | D | D |
Material comparison at 20 °C
Resistance overview
PETG is not resistant (D) to Aqua Regia and should not be used in direct contact. The chemical is expected to cause rapid degradation, which can include dissolution, cracking, severe swelling, or complete structural failure of the material.
Application context
Aqua Regia is commonly encountered in metal finishing and laboratory work. PETG (Polyethylene terephthalate glycol (co-polyester)) is a thermoplastic typically used for tanks, piping, containers and liners. Because Aqua Regia is classified as corrosive, the choice of containment material is especially critical to prevent leaks, equipment damage, and safety hazards.
Practical recommendation
PETG is not recommended for use with Aqua Regia. The D rating indicates that the material will suffer rapid and severe degradation, which may include cracking, dissolution, severe swelling, or complete structural failure. Using this combination risks equipment damage, leaks, and potential safety incidents. Consider using ECTFE/ETFE, PTFE instead, which are rated A for this chemical and offer reliable long-term performance.
Did you know?
In industrial practice, PETG components exposed to Aqua Regia are typically inspected for swelling, discoloration, or loss of mechanical strength as early indicators of chemical attack.
Materials rated A or B at 20 °C
- Fluoropolymers
- PTFE A, FEP B, ECTFE/ETFE A
About PETG
PETG is a co-polyester for clear containers. Strong acids and alkalis and most organic solvents attack it.
Rating scale
- A very good resistance
- B good resistance
- C limited resistance
- D not resistant
- – no data
- K no general statement possible
A rating marked * is an estimate in the source, not a test result. An estimate is given as one value without a temperature.
About this data
The ratings come from the chemical resistance list published by Bürkle GmbH, which compiled them from raw-material manufacturers’ data. They describe laboratory tests on the raw material at 20 °C and 50 °C.
A finished part also sees pressure, mechanical stress, welds and mixtures that a laboratory test does not. Treat the rating as a first filter and test under your own conditions before relying on it.