Rating
| Concentration | 20 °C | 50 °C | Remark |
|---|---|---|---|
| concentration not stated | D | D |
Material comparison at 20 °C
Resistance overview
LDPE is not resistant (D) to Butyric Acid and should not be used in direct contact. The chemical is expected to cause rapid degradation, which can include dissolution, cracking, severe swelling, or complete structural failure of the material.
Application context
Butyric Acid is commonly encountered in water treatment and laboratory work. LDPE (Low-density polyethylene) is a thermoplastic typically used for tanks, piping, containers and liners. Because Butyric Acid is classified as corrosive, the choice of containment material is especially critical to prevent leaks, equipment damage, and safety hazards.
Practical recommendation
LDPE is not recommended for use with Butyric Acid. The D rating indicates that the material will suffer rapid and severe degradation, which may include cracking, dissolution, severe swelling, or complete structural failure. Using this combination risks equipment damage, leaks, and potential safety incidents. Consider using ECTFE/ETFE, FEP, PTFE instead, which are rated A for this chemical and offer reliable long-term performance.
Did you know?
Chemical resistance testing according to DIN and ISO standards typically evaluates weight change, dimensional change, and retention of tensile strength after immersion.
Materials rated A or B at 20 °C
- Thermoplastics
- PVC Rigid B, Polysulfone B
- Fluoropolymers
- PTFE A, PVDF A, FEP A, ECTFE/ETFE A
- Metals
- SS 316 A, SS 304 A, Aluminium A
About LDPE
Low-density polyethylene has a similar profile to HDPE but is softer and more permeable, so solvents swell it sooner. Continuous service is usually limited to about 60 °C.
Rating scale
- A very good resistance
- B good resistance
- C limited resistance
- D not resistant
- – no data
- K no general statement possible
A rating marked * is an estimate in the source, not a test result. An estimate is given as one value without a temperature.
About this data
The ratings come from the chemical resistance list published by Bürkle GmbH, which compiled them from raw-material manufacturers’ data. They describe laboratory tests on the raw material at 20 °C and 50 °C.
A finished part also sees pressure, mechanical stress, welds and mixtures that a laboratory test does not. Treat the rating as a first filter and test under your own conditions before relying on it.