Rating
| Concentration | 20 °C | 50 °C | Remark |
|---|---|---|---|
| concentration not stated | D | D |
Material comparison at 20 °C
Resistance overview
Polycarbonate is not resistant (D) to Butyric Acid and should not be used in direct contact. The chemical is expected to cause rapid degradation, which can include dissolution, cracking, severe swelling, or complete structural failure of the material.
Application context
Butyric Acid is commonly encountered in metal finishing and chemical processing. Polycarbonate (Polycarbonate) is a thermoplastic typically used for tanks, piping, containers and liners. Because Butyric Acid is classified as corrosive, the choice of containment material is especially critical to prevent leaks, equipment damage, and safety hazards.
Practical recommendation
Polycarbonate is not recommended for use with Butyric Acid. The D rating indicates that the material will suffer rapid and severe degradation, which may include cracking, dissolution, severe swelling, or complete structural failure. Using this combination risks equipment damage, leaks, and potential safety incidents. Consider using ECTFE/ETFE, FEP, PTFE instead, which are rated A for this chemical and offer reliable long-term performance.
Did you know?
Polycarbonate is commonly chosen for tanks, piping, containers and liners because of its combination of chemical resistance, mechanical strength, and cost-effectiveness.
Materials rated A or B at 20 °C
- Thermoplastics
- PVC Rigid B, Polysulfone B
- Fluoropolymers
- PTFE A, PVDF A, FEP A, ECTFE/ETFE A
- Metals
- SS 316 A, SS 304 A, Aluminium A
About Polycarbonate
Polycarbonate is attacked by alkalis, amines, ketones, esters and many organic solvents, and it stress-cracks under load in contact with them.
Rating scale
- A very good resistance
- B good resistance
- C limited resistance
- D not resistant
- – no data
- K no general statement possible
A rating marked * is an estimate in the source, not a test result. An estimate is given as one value without a temperature.
About this data
The ratings come from the chemical resistance list published by Bürkle GmbH, which compiled them from raw-material manufacturers’ data. They describe laboratory tests on the raw material at 20 °C and 50 °C.
A finished part also sees pressure, mechanical stress, welds and mixtures that a laboratory test does not. Treat the rating as a first filter and test under your own conditions before relying on it.