Rating
| Concentration | 20 °C | 50 °C | Remark |
|---|---|---|---|
| concentration not stated | D | D |
Material comparison at 20 °C
Resistance overview
EPDM is not resistant (D) to Piperidine and should not be used in direct contact. The chemical is expected to cause rapid degradation, which can include dissolution, cracking, severe swelling, or complete structural failure of the material.
Application context
Piperidine is commonly encountered in chemical processing and metal finishing. EPDM (Ethylene propylene diene rubber) is an elastomer typically used for seals, O-rings, hoses and flexible connections. Because Piperidine is classified as corrosive, the choice of containment material is especially critical to prevent leaks, equipment damage, and safety hazards.
Practical recommendation
EPDM is not recommended for use with Piperidine. The D rating indicates that the material will suffer rapid and severe degradation, which may include cracking, dissolution, severe swelling, or complete structural failure. Using this combination risks equipment damage, leaks, and potential safety incidents. Consider using FEP, PTFE, Aluminium instead, which are rated A for this chemical and offer reliable long-term performance.
Did you know?
Ethylene propylene diene rubber was first developed in the 1960s and remains one of the most widely used elastomers in chemical handling equipment.
Materials rated A or B at 20 °C
- Thermoplastics
- PP B, Acetal (POM) B
- Fluoropolymers
- PTFE A, PVDF B, FEP A
- Metals
- SS 316 A, SS 304 A, Aluminium A
About EPDM
EPDM resists water, steam, alkalis, ketones and alcohols. Mineral oils, fuels and aromatic solvents swell it severely.
Rating scale
- A very good resistance
- B good resistance
- C limited resistance
- D not resistant
- – no data
- K no general statement possible
A rating marked * is an estimate in the source, not a test result. An estimate is given as one value without a temperature.
About this data
The ratings come from the chemical resistance list published by Bürkle GmbH, which compiled them from raw-material manufacturers’ data. They describe laboratory tests on the raw material at 20 °C and 50 °C.
A finished part also sees pressure, mechanical stress, welds and mixtures that a laboratory test does not. Treat the rating as a first filter and test under your own conditions before relying on it.