Rating
| Concentration | 20 °C | 50 °C | Remark |
|---|---|---|---|
| anhydrous | B | B | pitting risk |
Material comparison at 20 °C
Resistance overview
SS 304 shows good but limited resistance (B) to Hydrogen Chloride Gas at anhydrous at 20 °C. The material can be used in contact with this chemical, but minor effects such as slight swelling or a small reduction in mechanical properties may occur over extended exposure periods. Regular inspection of components in service is advisable. The rating remains stable between 20 °C and 50 °C, which means this material can also handle moderately elevated process temperatures without additional risk. Note that the source flags a risk of pitting or stress-corrosion cracking for this combination, which is particularly relevant for pressure-bearing or structurally loaded components.
Application context
Hydrogen Chloride Gas is commonly encountered in pulp and paper and chemical processing. SS 304 (Stainless steel 1.4301 (AISI 304)) is a metal typically used for vessels, heat exchangers, fittings and structural components. Because Hydrogen Chloride Gas is classified as corrosive, the choice of containment material is especially critical to prevent leaks, equipment damage, and safety hazards.
Practical recommendation
SS 304 is suitable for use with Hydrogen Chloride Gas under normal conditions, but some minor effects on the material are expected over time. Periodic monitoring for swelling, softening, or weight change is recommended, especially for long-service components. For safety-critical or long-life applications, consider HDPE, PP, PVC Rigid instead, which are rated A for this chemical.
Did you know?
Chemical resistance testing according to DIN and ISO standards typically evaluates weight change, dimensional change, and retention of tensile strength after immersion.
Materials rated A or B at 20 °C
Based on the row for anhydrous, 20 °C.
- Thermoplastics
- HDPE A, PP A, PVC Rigid A
- Fluoropolymers
- PTFE A, PVDF A, FEP A
- Elastomers
- EPDM A, Viton (FPM) A
- Metals
- SS 316 B
About SS 304
Stainless steel 304 (1.4301) resists oxidising acids and most organic chemicals. Chlorides cause pitting and stress-corrosion cracking.
Rating scale
- A very good resistance
- B good resistance
- C limited resistance
- D not resistant
- – no data
- K no general statement possible
A rating marked * is an estimate in the source, not a test result. An estimate is given as one value without a temperature.
About this data
The ratings come from the chemical resistance list published by Bürkle GmbH, which compiled them from raw-material manufacturers’ data. They describe laboratory tests on the raw material at 20 °C and 50 °C.
A finished part also sees pressure, mechanical stress, welds and mixtures that a laboratory test does not. Treat the rating as a first filter and test under your own conditions before relying on it.