Rating
| Concentration | 20 °C | 50 °C | Remark |
|---|---|---|---|
| aqueous | B | – | |
| saturated | B | – |
Material comparison at 20 °C
Resistance overview
SS 316 maintains a consistent rating of B across all 2 tested concentrations (aqueous, saturated) of Calcium Hypochlorite at 20 °C. The fact that the rating does not change with concentration within the tested range simplifies material selection, though the boundary conditions beyond this range remain untested. The rating remains stable between 20 °C and 50 °C, which means this material can also handle moderately elevated process temperatures without additional risk.
Application context
Calcium Hypochlorite is commonly encountered in pulp and paper and chemical processing. SS 316 (Stainless steel 1.4401 (AISI 316)) is a metal typically used for vessels, heat exchangers, fittings and structural components. Because Calcium Hypochlorite is classified as corrosive, the choice of containment material is especially critical to prevent leaks, equipment damage, and safety hazards.
Practical recommendation
SS 316 is suitable for use with Calcium Hypochlorite under normal conditions, but some minor effects on the material are expected over time. Periodic monitoring for swelling, softening, or weight change is recommended, especially for long-service components. For safety-critical or long-life applications, consider HDPE, LDPE, Nylon (PA) instead, which are rated A for this chemical.
Did you know?
In industrial practice, SS 316 components exposed to Calcium Hypochlorite are typically inspected for swelling, discoloration, or loss of mechanical strength as early indicators of chemical attack.
Materials rated A or B at 20 °C
Based on the row for saturated, 20 °C.
- Thermoplastics
- HDPE A, PP A, PVC Rigid B, LDPE A, Nylon (PA) A, Acetal (POM) A, Polystyrene B, Polysulfone A, PMP A, SAN A
- Fluoropolymers
- PTFE A, PVDF A, FEP A, ECTFE/ETFE A
- Elastomers
- EPDM B, Viton (FPM) B
About SS 316
Stainless steel 316 (1.4401) contains molybdenum, which improves resistance to chlorides over 304. Hydrochloric acid and other halide acids still cause pitting.
Rating scale
- A very good resistance
- B good resistance
- C limited resistance
- D not resistant
- – no data
- K no general statement possible
A rating marked * is an estimate in the source, not a test result. An estimate is given as one value without a temperature.
About this data
The ratings come from the chemical resistance list published by Bürkle GmbH, which compiled them from raw-material manufacturers’ data. They describe laboratory tests on the raw material at 20 °C and 50 °C.
A finished part also sees pressure, mechanical stress, welds and mixtures that a laboratory test does not. Treat the rating as a first filter and test under your own conditions before relying on it.